New rubber compound and precise air cells prevent gauge loss and provide great rebound property of the compressible layer.

Testing Method

The permanent change in blanket thickness after it has been stressed 0.19mm for 24 hours and released.

Assessment

S-PRIAs show lowest deformation that helps to maintain print quality and register control for longer time.

Testing Method

The strip of paper is attached on the sheet to increase its thickness to 0.4 mm. This sheet passes through the press, then the blanket is intentionally smashed. The press continues to print on 0.1 mm sheet. The test measures the change in ink transfer after smash.

Type of Paper	: Coated paper 128g/sqm
Ink	: Conventional Black
Pattern	: 100％ Solid (Density 1.5)
Printing Pressure (B/I)	: 15/100mm

Assessment

S-PRIAs show lowest change and quick recovery, and that proves great resistant to smash and mechanical shock.

Superior surface-rubber quality offers outstanding paper-release.
In addition, a reduction of paper dust buildup improves efficiency.

Testing Method

The amount of curl height at the tail of sheet.

Type of Paper	: Coated paper 128g/sqm
Ink	: Conventional Black
Pattern	: 100％ Solid (Density 1.5)
Printing Pressure (B/I)	: 15/100mm

Assessment

The amount of curl in S-PRIAs is minimal and both blankets provide outstanding paper-release.

Newly developed surface rubber offers excellent ink transfer that makes further improvement in half-tone dot reproduction.
With better solid density, both blankets produce outstanding printing.

Assessment

The amount of dot gain with both the S-PRIAs is minimal and half-dot printing is outstanding.